Nuclear Grade Disposable Gel Styrene-Based
Ultra-Uniform Mixed-bed Resin for Ultrapure Water Polishing Process
(Non-Regenerative)
International Equivalent Models:
Dower MR-3, Amberlite UP-6150, MR-450
| TECH-INDEXES: | SPECIFICATIONS: |
| Matrix: | Styrene-divinylbenzene copolymer |
| Functional groups: | _HSO3- | -N+(CH3)3 |
| Physical form: | Amber transparent spherical beads |
| Ionic form as shipped: | H+ | OH- form |
| Total bulk exchange capacity: | ≥1.7mmol/ml(H+ Cation Resin); ≥1.3mmol/ml(OH- Anion Resin) |
| Ratio of cation to anion resin: | 1:1.8 |
| Moisture bulk density: | 0.69g/ml |
| Uniformity coefficient: | ≤1.2 |
| Chemical stability: | Insoluble in water, diluted acid nor in alkali |
| PH: | 1~14 |
| Maximum operating temperature: | 60°C |
| Minimum bed depth: | 700mm |
| Operating service velocity: | 8~20 m/h |
NOTE:
During the process of synthesizing this resin, the ionic transition rate of H+ and OH- is quite high.
Also, exposure to air for a long time will cause this resin to absorb a large amount of carbon dioxide, which will affect the operational performance and usability of the resin. Therefore, once opened, it needs to be used as soon as possible, and the unused parts must be carefully sealed.
In addition, the product should neither be exposed to air nor direct sunlight.