Nuclear Grade Gel Styrene-Based
Mixed Resins(Cation:Anion=1:1) for Nuclear Plant Water Purification Systems
| TECH-INDEXES: | SPECIFICATIONS: |
| Matrix: | Styrene-divinylbenzene copolymer |
| Functional groups: | _HSO3- | -N+(CH3)3 |
| Physical form: | Earthy yellow transparent spherical beads |
| Ionic form as shipped: | H+ | OH- form |
| Ratio of cation to anion: | 1.0 | 1.0 |
| Moisture content(%) | 50-58 | 60-70 |
| Total bulk exchange capacity(mmol/ml): | ≥1.90 | ≥0.90 |
| Moisture bulk density(g/ml): | 0.75-0.85 | 0.65-0.70 |
| Moisture true density(g/ml): | 1.18-1.24 | 1.05-1.10 |
| Particle size(mm): | (0.40-1.20)≥95% |
| Chemical stability: | Insoluble in water, diluted acid nor in alkali |
| PH: | 1~14 |
| Maximum operating temperature: | 60°C |
| Minimum bed depth: | 700mm |
| Operating service velocity: | 8~20 m/h |
NOTE:
During the process of synthesizing this resin, the ionic transition rate of H+ and OH- is quite high.
Also, exposure to air for a long time will cause this resin to absorb a large amount of carbon dioxide, which will affect the operational performance and usability of the resin. Therefore, once opened, it needs to be used as soon as possible, and the unused parts must be carefully sealed.
In addition, the product should neither be exposed to air nor direct sunlight.